Browsing by Subject "Nanorods"
Now showing 1 - 3 of 3
Results Per Page
Sort Options
Item CdTe/CdSe/CdTe heterostructure nanorods and I-III-VI₂ nanocrystals: synthesis and characterization(2009-12) Koo, Bonil; Korgel, Brian Allan, 1969-Semiconductor nanocrystals are interesting candidates as new light-absorbing materials for photovoltaic (PV) devices. They can be dispersed in solvents and cheaply deposited at low-temperature on various substrates. Also, the nanocrystals have unique optical properties depending on their size due to the quantum size effect and moreover it is easy to uniformly control their stoichiometry. CdTe/CdSe/CdTe heterostructure nanorods and I-III-VI₂ nanocrystals were selected to synthesize and investigate in order to utilize the benefits of colloidal nanocrystals described above. Colloidal nanorods with linear CdTe/CdSe/CdTe heterojunctions were synthesized by sequential reactant injection. After CdTe deposition at the ends of initially formed CdSe nanorods, continued heating in solution leads to Se-Te interdiffusion across the heterojunctions and coalescence to decreased aspect ratio. The Se-Te interdiffusion rates were measured by mapping the composition profile using nanobeam energy dispersive X-ray spectroscopy (EDS). The rate of nanorod coalescence was also measured and compared to model predictions using a continuum viscous flow model. The synthetic method of monodisperse chalcopyrite (tetragonal) CuInSe₂ nanocrystals was also developed. The nanocrystals have trigonal pyramidal shape with one polar and three non-polar surface facets. When drop-cast onto carbon substrates, the nanocrystals self-assemble into close-packed monolayers with triangular (honeycomb) lattice structure. Moreover, the effect of excess Cu precursor (CuCl) was studied for the formation of monodisperse trigonal pyramidal CuInSe₂ nanocrystals. The formation mechanism of monodisperse trigonal pyramidal CuInSe₂ nanocrystals was suggested with regard to excess amount of CuCl precursor, based on the nucleationgrowth model of colloidal nanocrystal formation. A new wurtzite phase of CuInS₂, CuInSe₂, and Cu(InxGa1-x)Se₂ (CIGS) was observed in nanocrystals synthesized by heating metal precursors and Se-(or S-)urea in alkylamine. X-ray diffraction (XRD) showed the predominant phase to be wurtzite (hexagonal) instead of chalcopyrite (tetragonal). High resolution transmission electron microscopy (TEM), however, revealed polytypism in the nanocrystals, with the wurtzite phase interfaced with significant chalcopyrite domains.Item Study of stability of ZnO nanoparticles and growth mechanisms of colloidal ZnO nanorods(Texas A&M University, 2006-10-30) Lee, Kwang JikAfter hydrolyzing zinc acetate in methanol solution, spherical ZnO nanoparticles in the size range from about 2.5 to 5 nm were synthesized by maintaining a ZnO concentration of 0.02M. Compared to ZnO nanoparticles prepared via other methods, the particles prepared using our novel colloidal chemistry exhibit narrow size distribution and a high sensitivity to the surrounding environment. The structure and composition of the white powders precipitated from the colloidal solution can vary, depending on how the powder samples are prepared. Factors such as desorption and adsorption of methanol, binding of water and exposure to humid air have been studied to correlate to the structure and composition observed from the precipitated powder. Methanol desorption rate and excess KOH on the particle surface have played an important role in the structural changes. Furthermore, upon annealing, the white precipitate is recovered to wurtize ZnO. XRD and TEM are used to study the structural transformation of ZnO nanoparticles.Item Synthesis and characterization of silicon nanowires, silicon nanorods, and magnetic nanocrystals(2010-05) Heitsch, Andrew Theron; Korgel, Brian Allan, 1969-; Barbara, Paul F.; Ekerdt, John G.; Hwang, Gyeong S.; Mullins, C. B.Silicon nanowires, silicon nanorods, and magnetic nanocrystals have shown interesting size, shape, mechanical, electronic, and/or magnetic properties and many have proposed their use in exciting applications. However, before these materials can be applied, it is critical to fully understand their properties and how to synthesize them economically and reproducibly. Silicon nanowires were synthesized in high boiling point ambient pressure solvents using gold and bismuth nanocrystals seeds and trisilane as the silicon precursor. Reactions temperatures as low as 410°C were used to promote the solution-liquid-solid (SLS) growth of silicon nanowires. The silicon nanowires synthesis was optimized to produce 5 mg of silicon nanowires with average diameters of 30 nm and lengths exceeding 2 [mu]m by adjusting the silicon to gold ratio in the injection mixture and reaction temperature. Silicon nanorods were synthesized using a solution-based arrested-SLS growth approach where gold seeds, trisilane, and a dodecylamine were vital to the success. Dodecylamine was found to prevent gold seed coalescence at high temperatures -- creating small diameter rods -- and bond to the crystalline silicon surface -- preventing silicon nanorod aggregation. Furthermore, an etching strategy was developed using an emulsion of aqua regia and chloroform to remove the gold seeds from the silicon nanorods tip. A thin silicon shell surrounding the gold seed of the silicon nanorod was subsequently observed. Multifunctional colloidal core-shell nanoparticles of iron platinum or iron oxide encapsulated in fluorescent dye doped silica shells were also synthesized. The as-prepared magnetic nanocrystals are initially hydrophobic and were coated with a uniform silica shell using a microemulsion approach. These colloidal heterostructures have the potential to be used as dual-purpose tags, exhibiting a fluorescent signal that could be combined with enhanced magnetic resonance imaging contrast. Compositionally-ordered, single domain, antiferromagnetic L1₂ FePt₃ and ferromagnetic L1₀ FePt nanocrystals were synthesized by coating colloidally-grown Pt-rich or stoichiometricly equal Fe-Pt nanocrystals with thermally-stable SiO₂ and annealing at high temperature. Without the silica coating, the nanocrystals transform predominately into the L1₀ FePt phase due to interparticle diffusion of Fe and Pt atoms. Magnetization measurements of the L1₂ FePt₃ nanocrystals revealed two antiferromagnetic transitions near the bulk Neél temperatures of 100K and 160K. Combining L1₂ FePt₃ nanocrystals with L1₀ FePt nanocrystals was found to produce a constriction in field-dependent magnetization loops that has previously been observed near zero applied field in ensemble measurements of single domain silica-coated L1₀ FePt nanocrystals. Dipole interactions between FePt@SiO₂ nanoparticles with varying SiO₂ shell thickness was also explored.