Browsing by Subject "Mesoporous silica"
Now showing 1 - 2 of 2
Results Per Page
Sort Options
Item Mesoporous silica chips for harvesting the low molecular weight proteome from human serum(2009-12) Hu, Ye; Ferrari, Mauro, 1959-In this dissertation, mesoporous silica thin films with tunable features at the nanoscale were fabricated using the triblock copolymer template pathway, with the aim of specifically harvesting the low molecular weight peptides and proteins from human serum, which has been regarded as a potential source of diagnostic biomarkers for the early detection of disease. The superior properties of mesoporous silica have been demonstrated in applications which include chemical sensing, filtration, catalysis, drug-delivery and selective biomolecular uptake. These properties depend on the architectural, physical and chemical properties of the materials, which in turn are determined by the processing parameters in evaporation-induced self-assembly (EISA). Using the different polymer templates and polymer concentration in the precursor solution, various pore size distributions, pore structures and surface hydrophilicities were obtained and applied for nanotexture-selective recovery of low mass proteins. With the assistance of mass spectrometry and statistic analysis, we demonstrated the correlation between the nanophase characteristics of the mesoporous silica thin film and the specificity and efficacy of low mass proteome harvesting. In addition, to overcome the limitations of the pre-functionalization method in polymer selection, plasma ashing was used for the first time for the treatment of the mesoporous silica surface prior to chemical modification. Opposite surface charges due to the different functional groups used, resulted in a distinctive selectivity of the low molecular weight proteins from the serum sample. The mesoporous silica chips operate with extraordinary rapidity, high reproducibility, no sample pre-processing, and substantial independence from sample acquisition and storage temperature.In conclusion our study demonstrates that the ability to tune the physicochemical properties of mesoporous silica surfaces has the potential to promote the use of this material as a tool for the selective separation and concentration of the low molecular weight proteome from complex biological fluids.Item Thin film nanoporous silica and graphene based biofuel cells (iBFCs) for low-power implantable medical device applications(2010-08) Sharma, Tushar; Zhang, Xiaojing, Ph. D.; Milner, Thomas E.This thesis describes the fabrication and characterization of an inorganic catalyst based glucose Biofuel cell using nanoporous (mesoporous) silica thin-film as a functional membrane. The desired use of nanoporous silica based biofuel cell is for a blood vessel implantable device. Blood vessel implantable Biofuel Cells (iBFCs) are subjected to higher glucose concentrations and blood flow rates. However, reduction in the implant thickness is critical for the intra-vascular implantable Biofuel cells. Platinum thin-film (thickness: 25 nm) deposited on Silicon substrate (500 [mu]m) served as the anode while Graphene pressed on Stainless steel mesh (175 [mu]m) was used as the cathode. Control experiments involved the use of surfactant-coated polypropylene membrane (50 [mu]m) and Activated Carbon (198 [mu]m) electrodes. Preliminary results show that nanoporous silica thin film (270 nm) is capable of replacing the conventional polymer based membranes with an increased power density output of as high as 10 [mu]W/cm2 under physiological conditions. in-vitro (5 [mu]W/cm2) and in-vivo (10 [mu]W/cm2) experiments demonstrate the potential of ultra-thin iBFCs towards powering future medical implants.